发表刊物：MATERIALS LETTERS

收录刊物：SCIE、EI、Scopus

卷号：64

期号：11

页面范围：1291-1294

ISSN号：0167-577X

关键字：Unbalanced magnetron sputtering; Photoconductivity; Room-temperature ferromagnetism

摘要：The coexistence of ultraviolet (UV) photoconductivity (PC) and room-temperature ferromagnetism (RTFM) is observed in polycrystalline ZnO thin films deposited by unbalanced magnetron sputtering under high oxygen pressure. A significant increase in PC (similar to 870% to 40000%) is observed with increasing film thickness and the consequent structural disorder and film porosity. In contrast, the saturation magnetization (M(S)) at room temperature is found to decrease from 1.02 emu/g to 0.53 emu/g with increasing film thickness from 50 to 150 nm. (C) 2010 Elsevier B.V. All rights reserved.