点击次数：

论文类型：期刊论文

发表时间：2017-01-15

发表刊物：JOURNAL OF MEMBRANE SCIENCE

收录刊物：SCIE、EI、Scopus

卷号：522

页面范围：140-150

ISSN号：0376-7388

关键字：CAU-1 membrane; In-situ growth; CO2/N-2 separation

摘要：Facile synthesis of a thin tubular CAU-1 membrane was carried by simple in-situ solvothermal growth method through the use of the asymmetric alpha-Al2O3 tube support with the same metal centre as the CAU-1 framework. The solvent ratio, reactant concentration and support property were found significant for the formation of a dense and continuous pure CAU-1 membrane with highly permeable and selective CO2 towards N-2 and CH4. A high CO2 permeance of 0.80 x 10(-6) mol m(-2) s(-1) Pa-1 with separation factor of 14.8 was achieved for the M3 for 1:1 CO2/N-2 binary mixtures at room temperature. Both the increase of ethanol in the solvent mixture and reactant concentration were favourable for the formation of a dense and well intergrown pure CAU-1 membrane while their excessive increase led to impure NH2-MIL-53 formation. The composition and pore size of the support contributed to high permeance and selectivity of CAU-1 membrane for CO2/N-2 separation. (C) 2016 Elsevier B.V. All rights reserved.