点击次数：

论文类型：期刊论文

发表时间：2015-10-01

发表刊物：JOURNAL OF MEMBRANE SCIENCE

收录刊物：SCIE、EI、Scopus

卷号：491

页面范围：168-175

ISSN号：0376-7388

关键字：Boron-substituted; B-ZSM-11 zeolite membrane; Pervaporation; Ethanol/water mixture

摘要：Boron-substituted silicalite-2 (B-ZSM-11) membranes were prepared on seeded cheap macroporous alpha-Al2O3 tubes to separate ethanol from water by pervaporation. The incorporation of boron atom into MEL framework was confirmed by XRD and FTIR. The effects of B/Si ratio in the synthesis solution together with PV operation temperature and feed concentration on separation properties of the membranes were investigated. The B-ZSM-11 membrane prepared with B/Si ratio of 0.06 exhibited the highest separation factor of 35.0 with a total flux of 1.51 kg m(-2) h(-1) for 5 wt% ethanol/water mixtures at 60 degrees C. The total flux increased with increasing PV temperature from 30 to 75 degrees C and the separation factor showed the highest value at 60 degrees C. The separation factor decreased with feed concentration from 1 to 7 wt% and the total flux also showed the highest value for a 5 wt% mixture. It is demonstrated that the incorporation of boron atom into MEL structure improved separation performance of B-ZSM-11 membrane for ethanol/water solutions. On the other hand, the better hydrophobicity of B-ZSM-11 membranes, evidenced by contact angle measurements, is responsible for pervaporation performance for ethanol/water mixtures. (C) 2015 Elsevier B.V. All rights reserved.