点击次数：

论文类型：期刊论文

发表时间：2014-12-01

发表刊物：JOURNAL OF MEMBRANE SCIENCE

收录刊物：SCIE、EI、Scopus

卷号：471

页面范围：84-93

ISSN号：0376-7388

关键字：Seed-free synthesis; Zeolite NaA membrane; Deposition of APTES-Al2O3 particle; Coarse macroporous support; Dehydration of ethanol

摘要：A new strategy through deposition of 3-aminopropyltriethoxysilane (APTES) functionalized Al2O3 particles on a coarse macrosporous tube with big defect holes was reported for seed-free synthesis of zeolite NaA membranes. Prior to the deposition of Al2O3 particles onto the macroporous support, APTES was covalently functionalized onto the surface of Al2O3 particles, aiming at providing heterogeneous sites for the growth of NaA zeolites on the support surface by serving as linker between the support and the silica and aluminum sources. Large APTES-Al2O3 particles were firstly deposited on the support surface to reduce the surface roughness and the effective pore sizes, subsequently the small APTES-Al2O3 particles were deposited on the support to provide plenty of heterogeneous nucleation sites for the growth of zeolite NaA crystals. In this way, a thin and continuous APTES-Al2O3 layer was formed on the support. After one single hydrothermal synthesis, a thin and compact zeolite NaA membrane with thickness of 2 rim was achieved. The synthesized NaA membranes showed high fluxes of 3.73.9 kg m(-2) h(-1) with separation factors over 5000 in dehydrating the 90 wt% ethanol/10 wt% water mixtures at 75 degrees C. The strategy presented in this study was expected to extend for preparation of other types of thin zeolite membranes on such coarse symmetric rnacroporous supports. (C) 2014 Elsevier B.V. All rights reserved.