发表刊物：JOURNAL OF MEMBRANE SCIENCE

收录刊物：SCIE、EI、Scopus

卷号：285

期号：1-2

页面范围：258-264

ISSN号：0376-7388

关键字：silicalite-1 membrane; varying-temperature; stainless steel support; reproducibility; thermal stability

摘要：High-quality zeolite silicalite-1 membranes with a large area (78.5 cm(2)) were successfully prepared on porous, tubular stainless steel (PTSS) supports with optimized synthesis solution composition by a two-stage varying-temperature in situ synthesis. Compared with the synthesis at constant temperature (one-stage), the two-stage varying-temperature in situ synthesis (TSVTS) generated a thin and dense membrane, since a large number of new nuclei could form at low temperature, while the crystallization temperature was rapidly changed to a high temperature after completion of the nucleation period, a thin and continuous membrane would quickly formed on the support by the nuclei regrowth. The membranes were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and single-gas permeation. These results indicate that the membranes prepared by the TSVTS method exhibit high gas permeation performance and good reproducibility. H-2 permeance and H-2/n-C4H10 selectivity of the membranes by TSVTS method reached to 12.25 x 10(-7) mol/(m(2) sPa) and 46.1, respectively. And the yield of high-quality membranes with perm-selectivity of H-2/n-C4H10 larger than 25 (which is almost five times as large as the Knudsen factor) as a quality criterion reached to 70% of all preparations. By comparison of their permeability and reproducibility with those reported in the literature, it was revealed that the prepared membranes by TSVTS method were of good quality. Moreover, their thermal stability were tested in a gas mixture of ethylbenzene and hydrogen at high temperature, for an example, the membrane having the separation selectivity of hydrogen and ethylbenzene mixture as high as 190 is stable after 80h of run at 400 degrees C, suggesting the membrane is thermally durable for long time operation.(c) 2006 Elsevier B.V All rights reserved.