Synthesis and characterization of amorphous Al-Mg-B prepared by various deposition temperatures
点击次数：
论文类型：期刊论文
发表时间：2013-04-01
发表刊物：RARE METALS
收录刊物：EI、SCIE
卷号：32
期号：2
页面范围：159-164
ISSN号：1001-0521
关键字：Amorphous Al-Mg-B; Deposition temperature; Properties; Coated cutting tool
摘要：Amorphous Al-Mg-B thin films were synthesized via a combinatorial sputtering approach. The properties of Al-Mg-B films with the varying deposition temperature was investigated. The deposition temperature was found to dominate the hardness of the amorphous as-deposited film. The hardness increases with increasing deposition temperature and may even exceed that of crystalline AlMgB14 material. The high hardness may be attributed to the existence of randomly distributed B-12 icosahedra structure. Therefore, the thin film that was deposited on cemented carbide shows well-cutting performances in turning Ti alloy bar. At the same time, an appropriate method of pretreatment is the key to ensure the coating tool with the excellent adhesion by impact fracture test.