任职 : 国际磨粒技术学会(International Committee of Abrasive Technology, ICAT)委员,中国机械工程学会极端制造分会副主任、生产工程分会常务委员、微纳米制造技术分会常务委员,中国机械工程学会生产工程分会磨粒加工技术专业委员会副主任、切削加工专业委员会常委委员、精密工程与微纳技术专业委员会常委委员,中国机械工程学会特种加工分会超声加工技术委员会副主任,中国机械工程学会摩擦学分会微纳制造摩擦学专业委员会常务委员,中国机械工业金属切削刀具协会切削先进制造技术研究会常务理事、对外学术交流工作委员会副主任、切削先进制造技术研究会自动化加工技术与系统委员会副主任。

性别:男

毕业院校:西北工业大学

学位:博士

所在单位:机械工程学院

学科:机械制造及其自动化. 机械电子工程. 航空宇航制造工程

办公地点:机械工程学院5138

联系方式:0411-84706059

电子邮箱:kangrk@dlut.edu.cn

扫描关注

论文成果

当前位置: 中文主页 >> 科学研究 >> 论文成果

Microstructural evolution of soft magnetic 49Fe-49Co-2V alloy induced by drilling

点击次数:

论文类型:期刊论文

发表时间:2020-04-01

发表刊物:MATERIALS & DESIGN

收录刊物:EI、SCIE

卷号:189

ISSN号:0264-1275

关键字:49Fe-49Co-2V alloy; Drilling; Microstructural evolution; Microhardness; Strengthening mechanisms

摘要:Mechanical drilling can change the microstructure of the regions near the hole wall, remarkably affecting the working performance of precision parts. The present work investigated the microstructural evolution in the regions from the drilled hole wall to the inner matrix of the soft magnetic 49Fe-49Co-2V alloy after the common drilling experiments were carried out. The microstructures and microhardness in different regions near the hole wall along the radial direction were characterized with OM, SEM, TEM, EBSD and Vickers Microhardness tester. The experimental results show that the nearest region to the hole wall is constituted of nano-sized refined grains. It exhibits a disordered BCC phase due to the rapid cooling from the high temperature during the drilling, different from the dual-phase of BCC and B2 of the matrix. The second-nearest region to the hole wall is distributed by a huge number of dislocations, leading to a maximum in microhardness. The microstructural evolution contributes to the variation of the microhardness, which increases firstly, reaches a maximum, and then decreases to the level of the matrix with the distance increasing from the hole wall. This variation tendency is discussed in light of both refined grain-boundary strengthening and dislocation strengthening mechanisms. (C) 2020 The Authors. Published by Elsevier Ltd.