点击次数：

论文类型：期刊论文

发表时间：2011-03-01

发表刊物：JOURNAL OF ELECTRONIC MATERIALS

收录刊物：SCIE、EI

卷号：40

期号：3

页面范围：315-323

ISSN号：0361-5235

关键字：Al-Cu joint; Sn-9Zn-xAg; mechanical properties; electrochemical corrosion; corrosion potential

摘要：The effect of Ag content on the wetting behavior of Sn-9Zn-xAg on aluminum and copper substrates during soldering, as well as the mechanical properties and electrochemical corrosion behavior of Al/Sn-9Zn-xAg/Cu solder joints, were investigated in the present work. Tiny Zn and coarsened dendritic AgZn(3) regions were distributed in the Sn matrix in the bulk Sn-9Zn-xAg solders, and the amount of Zn decreased while that of AgZn3 increased with increasing Ag content. The wettability of Sn-9Zn-1.5Ag solder on Cu substrate was better than those of the other Sn-9Zn-xAg solders but worse than that of Sn-9Zn solder. The wettability of Sn-9Zn-1.5Ag on the Al substrate was also better than those of the other Sn-9Zn-xAg solders, and even better than that of Sn-9Zn solder. The Al/Sn-9Zn/Cu joint had the highest shear strength, and the shear strength of the Al/Sn-9Zn-xAg/Cu (x = 0 wt.% to 3 wt.%) joints gradually decreased with increasing Ag content. The corrosion resistance of the Sn-9Zn-xAg solders in Al/Sn-9Zn-xAg/Cu joints in 5% NaCl solution was improved compared with that of Sn-9Zn. The corrosion potential of Sn-9Zn-xAg solders continuously increased with increasing Ag content from 0 wt.% to 2 wt.% but then decreased for Sn-9Zn-3Ag. The addition of Ag resulted in the formation of the AgZn3 phase and in a reduction of the amount of the eutectic Zn phase in the solder matrix; therefore, the corrosion resistance of the Al/Sn-9Zn-xAg/Cu joints was improved.