STOICHIOMETRY SPLITTING IN THE NI-FE-AL TERNARY BETA-PHASE

Hits:

Indexed by:期刊论文

Date of Publication:1993-07-01

Journal:JOURNAL OF THE JAPAN INSTITUTE OF METALS

Included Journals:SCIE

Volume:57

Issue:7

Page Number:840-847

ISSN No.:0021-4876

Key Words:NIAL; STOICHIOMETRY; NICKEL-ALUMINUM-IRON TERNARY SYSTEM; LATTICE PARAMETER; SUBSTITUTION SITE; DEFECT HARDENING; SOLID SOLUTION HARDENING

Abstract:It is shown that the stoichiometry of the ternary beta phase in the Ni-Fe-Al system splits into two through the measurement on hardness distribution and through careful examination on the available lattice parameter data. The first stoichiometry lies on the compositions connecting NiAl and FeAl, whereas the second on those connecting NiAl and the Fe corner. The former is attributed to the situation where all the Al atoms preferentially occupy one of the two sublattices so that the compositions are expressed strictly as (Ni, Fe)Al. The latter case, on the other hand, is the situation where Fe atoms are evenly distributed among the two sublattice sites. The lattice parameter of the beta phase exhibits a negative deviation from the Vegard's law in the vicinity of the first stoichiometry but it shifts into a positive deviation as the aluminum concentration decreases. The reason for the negative deviation would be due to the increasing stability of the beta phase, while that for the positive deviation to the effect of miscibility gap exsisting in the Ni-Al-fe ternary bcc phase. There found three types of concentration dependence of solid solution hardening or defect hardening in the ternary beta phase, for which a rigorous explanation cannot be made by any of the conventional theoretical treatments.

Pre One:NiAl金属间化合物的缺陷强化

Next One:EFFECTS OF DEVIATION FROM STOICHIOMETRY AND BORON ADDITION ON CREEP-BEHAVIOR IN NIAL