点击次数：

论文类型：期刊论文

发表时间：2009-05-05

发表刊物：JOURNAL OF ALLOYS AND COMPOUNDS

收录刊物：SCIE、EI、Scopus

卷号：475

期号：1-2

页面范围：862-868

ISSN号：0925-8388

关键字：Flake-shaped barium titanate; Electromagnetic characteristics; Reflection loss

摘要：The flake-shaped barium titanate (FBT) was prepared by a modified sol-gel method, and their microstructure and electromagnetic (EM) properties (2-18 GHz) were investigated by means of differential thermal analysis (DTA), thermogravimetry analysis (TG), X-ray diffraction (XRD), scanning electronic microscope (SEM) and a network analyser. The reflection loss R of FBT (annealing at different temperatures from 700 to 1200 degrees C/paraffin composite samples with thickness of 1 mm and FBT (annealing at 1000 degrees C)/paraffin composite samples with different thickness from I to 5 mm were calculated in 2-18 GHz using the relative complex permittivity and permeability according to the transmit-line theory. It was found that the electromagnetic characteristics and the wave absorption properties of FBT were improved. The maximal reflection loss of FBT (annealing at 1000 degrees C)/paraffin composite sample reached -29.6 dB at 12 GHz with a matching thickness of 4 mm. (C) 2008 Elsevier B.V. All rights reserved.