Deformation patterns and fracture stress of beta-phase gallium oxide single crystal obtained using compression of micro-pillars
点击次数:
论文类型:期刊论文
发表时间:2019-02-01
发表刊物:JOURNAL OF MATERIALS SCIENCE
收录刊物:SCIE、EI
卷号:54
期号:3
页面范围:1958-1966
ISSN号:0022-2461
关键字:Deformation; Fracture; High resolution transmission electron microscopy; Single crystals; Transmission electron microscopy, Compressive strain; Deformation defects; Deformation pattern; Fracture stress; Gallium oxides; Lattice bending; Lattice plane; Micro Pillars, Gallium compounds
摘要:The deformation of single-crystal beta-phase gallium oxide (or -Ga2O3) micro-pillars under compression was investigated with the aid of transmission electron microscopy. High-density stacking faults were the dominant deformation defects in the plastically deformed micro-pillars. Micro-cracks were found along (200), (001) and (010) lattice planes and fracture occurred along (200) lattice plane when compressive strain was sufficiently great. Lattice bending was also observed in the fractured pillar. The average fracture stress and strain of -Ga2O3 being measured are 7.25 +/- 1.11GPa and 3.80 +/- 0.57%, respectively, which have never been reported previously.