- High temperature corrosion and microstructure deterioration of KHR35H radiant tubes in continuous annealing furnace
- 点击次数：
- 论文类型： 期刊论文
- 发表时间： 2012-04-01
- 发表刊物： ENGINEERING FAILURE ANALYSIS
- 收录刊物： SCIE、EI
- 卷号： 21
- 页面范围： 59-66
- ISSN号： 1350-6307
- 关键字： Heat resistant steel; Oxidation; Creep; Microstructure deterioration
- 摘要： High temperature corrosion and microstructure deterioration phenomenon of KHR35H radiant tubes had been investigated after a service life of approximately 2 years in annealing process. Analyses revealed that deterioration in mechanical properties of the radiant tube was caused primarily by significant growth of precipitates during high temperature service. Internal oxidation and simultaneously in situ carbides dissolution were responsible for the formation of large number of voids and microcracks at the inner wall of the tubes, which brought the reduction of effective thickness of the tube wall and may act as crack sources under either thermal shock or creep deformation. (C) 2011 Elsevier Ltd. All rights reserved.