发布时间：2019-10-21

论文类型：期刊论文

发表时间：2018-04-01

发表刊物：METALS

收录刊物：SCIE

卷号：8

期号：4

ISSN号：2075-4701

关键字：TiAl alloy; Zener-Hollomon parameter; Nb particle; fracture toughness

摘要：Hot compressive deformation behaviors of a powder metallurgy Ti-45Al-5Nb-0.4W/2Nb (at. %) were investigated at strain rates from 0.001 s(-1) to 1 s(-1) and temperatures from 1050 degrees C to 1200 degrees C. The Zener-Hollomon (Z) parameter can affect the hot deformation mechanism significantly. At a high Z condition, Nb particles played an important role in coordinating the deformation. At a low Z condition, deformation of Nb particles accompanied by dynamic recrystallization (DRX) can act as a dominant softening mechanism. The as-forged pancake exhibits a short rod-like particle-toughened equiaxed matrix. For notched three-point bending (3PB) tests, the fracture toughness of an Nb-particles-toughened high-Nb-containing duplex phase-gamma-TiAl alloy was hardly affected by the loading rate, presenting a peak fracture toughness of about 12.9 MPa.m(1/2). The toughness of the present alloy can be improved by ductile Nb particles. A model based on the Griffith-Orowan-Irwin relation was constructed, which is quite accurate to predict the facture toughness of the present specimen using tensile properties.