点击次数：

论文类型：期刊论文

发表时间：2017-03-01

发表刊物：INTERNATIONAL JOURNAL OF HEAT AND MASS TRANSFER

收录刊物：SCIE、EI

卷号：106

页面范围：1287-1293

ISSN号：0017-9310

关键字：Carbon nanotube; Thermal interface material; High temperature; Thermomechanical stress

摘要：Carbon nanotube arrays hold much potential for high-temperature thermal interface applications that require thermal stability and mechanical compliance. A 1D reference bar test rig designed for measurements at and substantially above room temperature is used to perform thermal cycling tests on CNT arrays and to measure their thermal interface resistance at temperatures up to 700 degrees C. The CNT arrays are synthesized and tested with both thermomechanically matched (Cu-Cu) and mismatched (alumina-Cu) interfaces to examine their mechanical compliance. For both cases, a moderate decrease in thermal interface resistance (TIR) occurs from room temperature to 700 degrees C. The results reveal good cyclic stability of CNT arrays in both cases, confirming their ability to accommodate large thermomechanical mismatch. Post-mortem analysis indicates that CNT free ends conform to the opposing Cu surface. In the Cu-Cu interface, only compressive deformation of the CNT arrays is observed. In the alumina-Cu interface, more complex thermomechanical deformation occurs that is hypothesized to be a combined effect of compressive loading and shear stress. (Cd) 2016 Published by Elsevier Ltd.