论文类型:期刊论文
发表时间:2015-02-01
发表刊物:POLYMERS FOR ADVANCED TECHNOLOGIES
收录刊物:SCIE、EI、Scopus
卷号:26
期号:2
页面范围:153-159
ISSN号:1042-7147
关键字:epoxy resin; DOPO; liquid oxygen compatibility; thermal stability
摘要:Bisphenol A and bisphenol F epoxy resins (BA and BF) were chemically modified by 9,10-Dihydro-9-oxa-10-phosphaphenanthrene-10-oxide to improve their liquid oxygen compatibility. The structures of the modified epoxy resins were confirmed by Fourier transform infrared spectroscopy. Significant enhancement of liquid oxygen compatibility for the modified resins was detected according to the liquid oxygen mechanical impact test. Thermogravimetric analysis showed that during the degradation in oxygen atmosphere, the modified resins exhibited much lower weight loss rate and possessed much higher char residues than the control ones. Based on limited oxygen index test, better flame retardancy was also observed for the modified resins. In addition, the modified BA system was more excellent than the modified BF system in liquid oxygen compatibility, thermal stability, and flame retardancy. X-ray photoelectron spectroscopy analysis showed that after the liquid oxygen impact, the modified resins was still in oxidation stage and the control ones already begun to decompose and char. It could be attributed to formation of the phosphoric oxyacid on the surface of the modified resins, which prevented decomposition and inhibited the reaction between the specimen and liquid oxygen. Copyright (c) 2014 John Wiley & Sons, Ltd.