发表刊物：RSC ADVANCES

收录刊物：SCIE、EI、Scopus

卷号：5

期号：15

页面范围：11325-11333

ISSN号：2046-2069

摘要：The bisphenol A epoxy resin was modified by the polycondensation between tetrabromobisphenol A and bisphenol A epoxy resin. After curing using 4,4'-diaminodiphenyl methane (DDM) and 4,4'-diaminodiphenyl sulfone (DDS), the liquid oxygen compatibility of bisphenol A epoxy resin and modified bisphenol A epoxy resin was measured by the mechanical impact test (ASTM D2512-95). The results suggested that the modified bisphenol A epoxy resin curing using 4,4'-diamino diphenylmethane (DDM) was compatible with liquid oxygen. The thermogravimetric analysis (TGA) revealed that the modified bisphenol A epoxy resin has lower temperatures of the initial degradation and the maximum mass loss rate compared with unmodified. The X-ray photoelectron spectroscopy (XPS) measurement results indicated that the C-C/H groups were oxidized to C-O-C/H and/or C=O groups during the impact process. The mechanical properties of all samples were measured at room temperature (RT) and nitrogen temperature (77 K). The flame-retardant modification of epoxy resin may be an effective way to obtain the compatible epoxy resin material with liquid oxygen.